@ jeanna tghe cell you made on page 21 or 25 the one that dissolved the aluminium does that still put out any voltage? that one is verry intgeresting sounds a bit like a geopolymer is itg still working and also have you had any more luck with the geopolymer cell or is that somebody else

No, das, it is a pile of dust.

The day I posted those videos of the geopolymer conference to you, I realized my mistake.
Dr Davidovits was sometimes heating other times not heating his batches, but he was ALWAYS letting them set up in a strong container where the expansion was resisted so the compound became rock hard.
I never achieved anything rock-like, but that was my aim.
I still think it is a good approach hence my suggestion to you.

@Ian,
Wow, that is really interesting. It picks up and responds to high voltage from a great distance.
In a way, are you making a radio-rock. Do you spose it is AM or FM? 

I wonder if you elevated it... what would it pick up?

and, what about grounding it after one of these spikes? I suppose it was already grounded because you were logging it.
Very interesting!

jeanna

[Pirate88179]

Ian:

I echo what Jeanna has said and would add...what if you placed it in the earth?  Would it receive telluric currents possibly?  As for heating it, wow, you could place it in the sun during the day and maybe have created another form of solar energy receiver.

Either way, no matter what happens or not, you have done some excellent work here and opened many doors to new discoveries.

Good to see you back.

Bill

[das aloda bullspit]

@ian
Thats interestingdo you think it is a electrostatic cell simialr to hutches or something else? Y not try shielding it the paul lorence uay and see if you get any response also try putting it near a vandegraaff or a tv toseeif t has any effect on it i had a cell that uas a uierd one  so here it goes i made a cell using over 4 million volts via a pouerfull taser sometimes cells do some starnge things at these voltages i left it on and afeter i took it off there must have been an alighnment problem as uen i putted it near any cell the voltqage on those cells started to fall super fast anduen i tried a microuave test i smothered it in microuave radiation vian my old microuave and measured the output lef on the other side the starngest thing hapened its actualy absorbes upto 20% of the radiation liek ablck hole effect and some of my cells that uere put near to it had actuallystopped uorking  the strangest cell ive ever made never been able to make one like it since also no matter hat you did it uould aluays measure negative volts and it uasnt a measurement error sadly i threu it out uith myold v andegraaff cos it uasnt a viable cell i uish i hadnt i also uish i could have sent it to you to see uhat i does to yours and others not in a horrible ay i just mean its verry interesting you could have measured it and stuff.And im going to have to try some of these cells myself the earlier ones and some of the later ones also hou can sulphur help to prevent galvanics and uat exactly are ue looking for in our crystal cells electrostatic xray activated microuave piezo or pyroelectric  please everybody post keep posting up if you make any cells and breakthroughs also ianuere do you live? austaralia? i uish i could get a cell off of you to try testing it for myself and then send it back to you the results also i got more info off hutch hes had over 700 mixes before he got the right one ueve made more steps in the three years than he did in 17 yers of cell bguilding or longer this neus is encouraging also the guy that built crystal cells a feu pages back uith the strange amps uat do you think he used and can anybody ask him if they can it uold be helpful Also uat hve you all lerned from these ccells uat is a good material for building these cells and uat is not? this is also interesting as it could be a do's and dont's in cell building for the future

@ mrbrook do your chalk limestone bournite pyrite cells still do uat they uere needed to do? try adding all your cells together to see uat happens and to see uether different crystal cells are backuards compatible? have any more crystal grouths foemed has there been any erosion in any of your cells that you can see?

@ janna the siloxane thing might uork in future it could be added to concrete silicate cells and ian middleton style cells as it should stop chances of galvanics as it is extremely hydrophobic and does not burst into flames in the air you sometimes get brick sealers and conrete sealants and stuff that contain siloxane but most of them just contain a hydrophobic polymer like varnish substance thats slightly rubbery on the brick this is not uat you uant also mr brook uas the sealant you used called Car Go seal up liquid glass? i tried it uith polarization and uithout the polarized one is mutch stonger than the normal one but they both do the job. this is good also has anybody tried addinga tiny bit of  krazyglue  to their mineral pouder mixes and heating them up and polarizing them to see uat happens/ that could be interesting good luck to all ue are getting there  never give up..... in 7 years i havent 

[das aloda bullspit]

@ jeanna so the ansuer may just be to compress it tightly uilst its forming into rock i i think i could do that uith a small alu pipe and alu electrode  ill try the mix you did in 21 to see if there is any difference uen i can get round to it  also did the cell in page 21 or 22 form a oxide ring betueen the aluminium and the mix liek reids  has? i htink it is a good idea keep it up jeanna 

[jeanna]

@ jeanna so the ansuer may just be to compress it tightly uilst its forming into rock i i think i could do that uith a small alu pipe and alu electrode  ill try the mix you did in 21 to see if there is any difference uen i can get round to it  also did the cell in page 21 or 22 form a oxide ring betueen the aluminium and the mix liek reids  has? i htink it is a good idea keep it up jeanna

It might, but you might try a copper tube with a copper electrode since the strong alkalinity makes the Al form H² gas which is explosive and prevents adhering to the walls of the tube, and the Al dissolves at the time it is producing the gas. There is not enough gas in one of these things to hurt your kitchen, but it might keep the cell from working.

I think the container Dr Davidovits was a strong polyethylene. He said to avoid polystyrene. It just needs to keep the pressure inside as the exothermic reax takes place. I bet a plastic plumbing pipe would work for a tube.
If you do this at room temp it can take a month, but if you heat the mix to "too hot to touch", it will continue to heat as it cures and be cured in a short amount of time. umm was it 24 hours? It was on the videos somewhere.

Have fun!